The invention discloses a method for attaching decorative stainless steel sheets on the surface of granite, comprising three steps of granite surface treatment, stainless steel sheet back processing and stainless steel sheet pasting. The method of the invention of granite surface was etched by alkali solution treatment, make the granite surface more easily bonded stainless steel sheet with fine grit on the back of the adhesive to fix, so after the adhesive between the stainless steel sheet and granite adhesive strong and lasting, the materials used are common materials, construction cost is low.
【技术实现步骤摘要】
一种在花岗石表面贴附装饰不锈钢片的方法
本专利技术涉及装修装饰领域,更确切地说,是一种在花岗石表面贴附装饰不锈钢片的方法。
技术介绍
花岗岩得天独厚的物理特性加上它美丽的花纹使他成为建筑的上好材料,素有“岩石之王”之称。许多需要耐风吹雨打或需要长存的地方或物品都是由花岗岩制成的。花岗岩结构均匀,质地坚硬,颜色美观,是优质建筑石料。抗压强度根据石材品种和产地不同而异,约为1000-3000公斤/厘米。花岗岩不易风化,颜色美观,外观色泽可保持百年以上,由于其硬度高、耐磨损,除了用作高级建筑装饰工程、大厅地面外,还是露天雕刻的首选之材。以花岗岩为原料的各种石材在建筑装饰上应用广泛,用于装饰的不锈钢片也是一种普遍使用的表面装饰材料。在日常的工程建设或者装修装饰过程中,很多场合需要将不锈钢片固定在花岗石表面。用钢钉固定会影响美观且工序复杂,而用一般的胶水粘贴则不锈钢片容易翘起、脱落。
技术实现思路
本专利技术主要是解决现有技术所存在的技术问题,从而提供一种在花岗石表面贴附装饰不锈钢片的方法。本专利技术的上述技术问题主要是通过下述技术方案得以解决的:一种在花岗石表面贴附装饰不锈钢片的方法,包含如下步骤:①用喷雾装置将浓度为60-68%的氢氧化钠溶液均匀喷涂在花岗石表面,2-3小时后再喷涂一次,2-3小时后用清水冲洗花岗石表面并自然晾干;②用JL-498快干胶在不锈钢片的背面形成纵横交错的粘接条,粘接条的宽度控制在2-4mm,粘接条的间距控制在3-15cm,然后立即在不锈钢片的背面均匀撒上细钢砂,细钢砂的颗粒大小为0.3-0.6mm,3-5分钟后抖去多余钢砂,粘接条上钢砂与 ...
【技术保护点】
一种在花岗石表面贴附装饰不锈钢片的方法,其特征在于,包含如下步骤:①用喷雾装置将浓度为60‑68%的氢氧化钠溶液均匀喷涂在花岗石表面,2‑3小时后再喷涂一次,2‑3小时后用清水冲洗花岗石表面并自然晾干;②用JL‑498快干胶在不锈钢片的背面形成纵横交错的粘接条,粘接条的宽度控制在2‑4mm,粘接条的间距控制在3‑15cm,然后立即在不锈钢片的背面均匀撒上细钢砂,细钢砂的颗粒大小为0.3‑0.6mm,3‑5分钟后抖去多余钢砂,粘接条上钢砂与不锈钢片粘贴牢固;③按重量份取白乳胶5‑7份、腻子粉4‑5份、水5‑7份,混合均匀后制成粘合剂,将粘合剂均匀涂布于花岗石表面,然后将步骤②制做完成的不锈钢片依次粘贴到花岗石上并压实,固化后即可。
【技术特征摘要】
1.一种在花岗石表面贴附装饰不锈钢片的方法,其特征在于,包含如下步骤:①用喷雾装置将浓度为60-68%的氢氧化钠溶液均匀喷涂在花岗石表面,2-3小时后再喷涂一次,2-3小时后用清水冲洗花岗石表面并自然晾干;②用JL-498快干胶在不锈钢片的背面形成纵横交错的粘接条,粘接条的宽度控制在2-4mm,粘接条的间距控制在3-15cm,然后立即在不锈钢片的背面均匀撒上细钢砂,细钢砂的颗粒大小为0.3-0.6mm,3-5分钟后抖去多余钢砂,粘接条上钢砂与不锈钢片粘贴牢固;③按...
【专利技术属性】
技术研发人员:万东方,刘志平,
申请(专利权)人:苏州科斯曼照明工程有限公司,
类型:发明
国别省市:江苏,32