The invention discloses a preparation method of high water absorption and water retention material, which uses potassium persulfate as initiator and biomass grafting acrylic series to prepare water absorbing resin. Water absorbent resin prepared with proper molecular weight, water absorption rate of up to 850 G - G - 1, the preparation method used in biomass cellulose containing considerable, has a positive effect on the lignin and hemicellulose components in soil fertility, improve soil microelement etc.. The preparation of high water absorbent and water retaining material with agricultural surplus can not only make the natural resource be utilized effectively, but also reduce the cost of high water absorbing and water retaining material and increase the composite function of the material.
【技术实现步骤摘要】
一种高吸水保水材料的制备方法
本专利技术涉及化工领域,具体涉及一种高吸水保水材料的制备方法。
技术介绍
高吸水性树脂是20世纪50年代开始发展起来的含强亲水基团的水溶胀型新型功能高分子材料,具有吸水容量大、吸水速度快、施压下不脱水、保水能力强的优点,应用范围较广。按原料来源不同,一般分为合成树脂系、淀粉接枝系和纤维素接枝系等三大类。纤维素接枝系因具有凝胶强度高、抗生物降解、耐盐性好、pH值易调节等优点,再加上纤维素来源广泛,有降低成本、环境友好、废弃物资源化利用的潜力。
技术实现思路
本专利技术目的在于,提供一种高吸水保水材料的制备方法,本专利技术采用的技术方案如下:一种高吸水保水材料的制备方法,其特征在于,由以下步骤制备而成:(1)称取成取1份生物质材料,20份纯净水装入三口圆底烧瓶,放置于恒温水浴锅内,用恒速搅拌器搅拌,80℃恒温30-50min,期间以1L/min的速度通入氮气,以排尽容器中的空气。(2)冷却至50℃,向反应容器中缓慢加入3份丙烯酸,5份丙烯酸钠,3份甲基丙烯酸,以及过硫酸钾作为引发剂,进行接枝共聚反应。待凝结后停止搅拌,继续通入氮气约2h,即得反应产物。进一步地,步骤(1)所述的生物质材料是由竹粉,秸秆粉,玉米芯混合组成。进一步地,所述的生物质材料经过粉碎机研磨至60-80目。进一步地,步骤(2)所述的过硫酸钾用量为0.3-0.5份,配制成质量分数为10%的溶液,以分液漏斗在1-1.5h内逐滴缓慢加入到反应器中。本专利技术相对于现有技术的有益效果是:本专利技术的高吸水保水材料制备方法,以过硫酸钾为引发剂,生物质接枝丙烯酸系列制备吸水树脂 ...
【技术保护点】
一种高吸水保水材料的制备方法,其特征在于,由以下步骤制备而成:(1)称取成取 1份生物质材料,20份纯净水装入三口圆底烧瓶, 放置于恒温水浴锅内,用恒速搅拌器搅拌,80℃恒温30‑50min,期间以1L/min的速度通入氮气, 以排尽容器中的空气;(2)冷却至50℃, 向反应容器中缓慢加入3份丙烯酸,5份丙烯酸钠,3份甲基丙烯酸,以及过硫酸钾作为引发剂, 进行接枝共聚反应。 待凝结后停止搅拌,继续通入氮气约2 h, 即得反应产物。
【技术特征摘要】
1.一种高吸水保水材料的制备方法,其特征在于,由以下步骤制备而成:(1)称取成取1份生物质材料,20份纯净水装入三口圆底烧瓶,放置于恒温水浴锅内,用恒速搅拌器搅拌,80℃恒温30-50min,期间以1L/min的速度通入氮气,以排尽容器中的空气;(2)冷却至50℃,向反应容器中缓慢加入3份丙烯酸,5份丙烯酸钠,3份甲基丙烯酸,以及过硫酸钾作为引发剂,进行接枝共聚反应。待凝结后停止搅拌,继续通入氮气约2h,即得反应产物...