The invention discloses a method for waste plastic recycling, the second step (2) in the waste plastics are classified according to the color, material and value, the third step (3) drying temperature per minute in the promotion once, until the maximum temperature, the fifth step (5) of the recycled products plastic glass plate, the beneficial effect of the invention is: the new method of waste plastic recycling waste plastic processing, solves the difficult, difficult management, waste of resources, through the method of waste plastics recycling, waste plastics can be recycled to use, great use of waste resources, at the same time, the invention the implementation is simple, adapt to various regions.
【技术实现步骤摘要】
一种废塑料循环利用的方法
本专利技术涉及一种循环利用领域,具体为一种废塑料循环利用的方法。
技术介绍
塑料是指以树脂(或在加工过程中用单体直接聚合)为主要成分,以增塑剂、填充剂、润滑剂、着色剂等添加剂为辅助成分,在加工过程中能流动成型的材料。塑料为合成的高分子化合物,可以自由改变形体样式。塑料是利用单体原料以合成或缩合反应聚合而成的材料,由合成树脂及填料、增塑剂、稳定剂、润滑剂、色料等添加剂组成的,它的主要成分是合成树脂。在现实中对废塑料一般采用掩埋或焚烧的办法处理,这样不仅污染环境,也造成了资源的浪费。
技术实现思路
本专利技术的目的在于提供一种废塑料循环利用的方法,以解决上述
技术介绍
中提出的问题。本专利技术的目的是通过下述技术方案予以实现:一种废塑料循环利用的方法,其特征在于,包括以下步骤:(1)第一步:将收集的废塑料通过清洗机进行清洗;(2)第二步:将(1)中清洗干净的废塑料进行分类;(3)第三步:将(2)中分类好的废塑料进行干燥,干燥温度25摄氏度-30摄氏度,干燥时间0.5-1小时,干燥环境通风良好;(4)第四步:将(3)干燥好的废塑料通过粉碎机进行粉碎,粉碎粒大小为10mm-20mm;(5)第五步:将(4)倒入塑料再生颗粒机内进行废塑料的再生,达到循环利用的目的。在本专利技术一个较佳的实施例中,所述第二步(2)中废塑料按照颜色、材料和价值进行分类。在本专利技术一个较佳的实施例中,所述第三步(3)中的干燥温度每分钟提升一度,直至最高温度。在本专利技术一个较佳的实施例中,所述第五步(5)中的再生产品为塑料玻璃板。本专利技术的有益效果是:该新型一种废塑料 ...
【技术保护点】
一种废塑料循环利用的方法,其特征在于,由如下步骤组成:(1)第一步:将收集的废塑料通过清洗机进行清洗;(2)第二步:将(1)中清洗干净的废塑料进行分类;(3)第三步:将(2)中分类好的废塑料进行干燥,干燥温度25摄氏度‑30摄氏度,干燥时间0.5‑1小时,干燥环境通风良好;(4)第四步:将(3)干燥好的废塑料通过粉碎机进行粉碎,粉碎粒大小为10mm‑20mm;(5)第五步:将(4)倒入塑料再生颗粒机内进行废塑料的再生,达到循环利用的目的。
【技术特征摘要】
1.一种废塑料循环利用的方法,其特征在于,由如下步骤组成:(1)第一步:将收集的废塑料通过清洗机进行清洗;(2)第二步:将(1)中清洗干净的废塑料进行分类;(3)第三步:将(2)中分类好的废塑料进行干燥,干燥温度25摄氏度-30摄氏度,干燥时间0.5-1小时,干燥环境通风良好;(4)第四步:将(3)干燥好的废塑料通过粉碎机进行粉碎,粉碎粒大小为10mm-20mm;(5)第五步:将(4)倒入...
【专利技术属性】
技术研发人员:张瑞华,
申请(专利权)人:江西瑞晶家饰有限公司,
类型:发明
国别省市:江西,36
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。