The invention discloses a preparation method of capacitor with high crystallinity of biaxially oriented polypropylene film capacitor, the characteristics of the isotacticity of more than 98%, ash content is less than 15ppm, 2.0g/10min ~ 3.2g/10min melt index polypropylene resin material, the temperature and cooling rate and stress for high temperature resistant polypropylene film capacitor with high crystallinity the capacitance by the thin film prepared by the invention has light weight, low loss, good stability, excellent electrical insulation characteristics and mechanical properties, have high temperature performance, the capacitor with this film made in the run in 110 DEG C for a long time in bad environment.
【技术实现步骤摘要】
电容器用高结晶度双向拉伸聚丙烯电容膜的研制方法
本专利技术属于仅用碳-碳不饱和键反应得到的高分子化合物的制备方法，涉及一种电容器用高结晶度双向拉伸聚丙烯电容膜的制造方法，制得的电容器可在110℃的恶劣环境下长期运行。
技术介绍
现有的聚丙烯电容薄膜，由于其内部微观结构等原因，由于横向收缩率相对偏大，在金属化电容器制作与使用过程中，易造成的缺陷有：两端金属层与薄膜表面金属度层连接不好，引起介质损耗角正切增大，电容器温度升高，使电容器易击穿，且由于横向收缩严重，造成电容器容量下降，同时现有电容膜的耐压性能相对偏低，拉伸强度偏小，耐温性能差。
技术实现思路
针对上述情况，本专利技术的目的在于提供一种热稳定性好、耐高温、拉伸强度大的高结晶度双向拉伸聚丙烯电容膜及其生产方法。本专利技术得到的高结晶度聚丙烯电容薄膜，120℃下静置15分钟时的横向热收缩率≤0.2%、纵向热收缩率≤3.6%、横向拉伸强度≥300MPa、纵向拉伸强度≥200MPa，横向弹性模量≥4000N/mm2、纵向弹性模量≥2500N/mm2，制得的电容器可在110℃的恶劣环境下长期稳定运行。具体实施方式①供料：取电工级聚丙烯原料，通过真空吸料系统，经金属检测器被吸到挤出机上方料斗内，进行自动给料。②挤出塑化：挤出机温度为210℃～245℃，步骤①中的聚丙烯原料通过挤出机后被加热熔化，并挤出形成熔融均匀的粘流态熔体。③计量：将步骤②中得出的粘流态熔体经过计量泵后，变成等温、等压、等量的熔体进入过滤器。④过滤：采用10微米过滤网对熔体进行过滤，滤去熔体中的杂质及未熔物。⑤模头定型：模头各区温度均设定为245...
【技术保护点】
一种高结晶度双向拉伸聚丙烯电容膜，其特征是：120℃下静置15分钟时的横向热收缩率≤0.2%、纵向热收缩率≤3.6%、横向拉伸强度≥300MPa、纵向拉伸强度≥200MPa，横向弹性模量≥4000N/mm
【技术特征摘要】
1.一种高结晶度双向拉伸聚丙烯电容膜，其特征是：120℃下静置15分钟时的横向热收缩率≤0.2%、纵向热收缩率≤3.6%、横向拉伸强度≥300MPa、纵向拉伸强度≥200MPa，横向弹性模量≥4000N/mm2、纵向弹性模量≥2500N/mm2。2.一种高结晶度双向拉伸聚丙烯电容膜的生产方法，其特征包括如下步骤：①供料：采用等规度为98%～99%、灰分含量小于15ppm、熔融指数为2.0g/10min～3.2g/10min的聚丙烯树脂材料；②熔融挤出:将聚丙烯原料通过挤出机加热溶化，经模头形成等温等压熔体；③熔体冷却铸片成型：将等温等压的熔体经冷却辊冷却定型，制得厚片；④双向拉伸：将制得的铸片通过纵向拉伸机进行预热、拉伸、定型，制得厚膜；再将厚膜通过横向拉伸机进行预热、拉伸、定型，制得薄...
【专利技术属性】
技术研发人员：徐经楼，陈银平，陈银满，
申请(专利权)人：江苏中立方实业有限公司，
类型：发明
国别省市：江苏,32