The invention relates to a heat resistant grease, including poly alpha olefin ester oil, sebacic acid, lithium hydroxide mixture, tricresyl phosphate, two tungsten sulfide, water, essence, mass fraction of each component is poly alpha olefin ester oil 20 30, 11, 5 sebacic acid lithium hydroxide mixture of 3, 8 tricresyl phosphate 2 5, two 1.5, 3.9 pure tungsten sulfide 26 30, 1.8 2.1 flavor. The heat-resistant grease of the present invention adopts advanced biological technology, which is a high performance grease used for plastic gears and metal sliding parts, and contains special polymers, so that the utility model has excellent heat resistance. High temperature resistance, high viscosity, not easy to run oil, durable and efficient.
【技术实现步骤摘要】
一种耐热型润滑脂
本专利技术涉及一种润滑材料，具体地讲，本专利技术涉及一种耐热型润滑脂。
技术介绍
润滑脂是为了解决设备在运转时产生离心力的状态下，为减少设备摩擦磨损需要的一种润滑材料。润滑脂是在基础油中分散纤维状的增稠剂而制成半固体状的润滑剂，与润滑油相比，易附着于润滑部、不易流出。因此，可将润滑系统制成简单的结构，主要用于滚动轴承、滑动轴承、滚珠丝杠、直线运动引导件、齿轮等机械元件的润滑，广泛用于工业用机械、输送用机械系统等。
技术实现思路
针对现有技术中存在的上述不足，本专利技术所要解决的技术问题是提供一种效果好的耐热型润滑脂。本专利技术解决其技术问题所采用的技术方案是：提供一种耐热型润滑脂，包括聚α-烯烃酯类油、癸二酸、氢氧化锂混合物、磷酸三甲酚酯、二硫化钨、纯水、香精，各组分的质量份数为：聚α-烯烃酯类油20-30、癸二酸5-11、氢氧化锂混合物3-8、磷酸三甲酚酯2-5、二硫化钨1.5-3.9、纯水26-30、香精1.8-2.1。作为优选，所述的耐热型润滑脂，其特征在于：所述耐热型润滑脂还包括聚α-烯烃酯类油20、癸二酸5、氢氧化锂混合物3、磷酸三甲酚酯2、二硫化钨1.5、纯水26、香精1.8。作为优选，所述的耐热型润滑脂，其特征在于：所述香精优选为柠檬香精，改善耐热型润滑脂味道。作为优选，所述的耐热型润滑脂的制备方法，按照质量分数称取原料：聚α-烯烃酯类油、癸二酸、氢氧化锂混合物、纯水加入反应釜中，加热至150-180℃搅拌2.5h，然后加入磷酸三甲酚酯、二硫化钨降温至60-90℃搅拌，适当加入香精，搅拌均匀得到白色晶透的粘性膏状体，即得本实施例...
【技术保护点】
一种耐热型润滑脂，其特征在于：包括聚α‑ 烯烃酯类油、癸二酸、氢氧化锂混合物、磷酸三甲酚酯、二硫化钨、纯水、香精，各组分的质量份数为：聚α‑ 烯烃酯类油20‑30、癸二酸5‑11、氢氧化锂混合物3‑8、磷酸三甲酚酯2‑5、二硫化钨1.5‑3.9、纯水26‑30、香精1.8‑2.1。
【技术特征摘要】
1.一种耐热型润滑脂，其特征在于：包括聚α-烯烃酯类油、癸二酸、氢氧化锂混合物、磷酸三甲酚酯、二硫化钨、纯水、香精，各组分的质量份数为：聚α-烯烃酯类油20-30、癸二酸5-11、氢氧化锂混合物3-8、磷酸三甲酚酯2-5、二硫化钨1.5-3.9、纯水26-30、香精1.8-2.1。2.根据权利要求1所述的耐热型润滑脂，其特征在于：所述耐热型润滑脂还包括聚α-烯烃酯类油20、癸二酸5、氢氧化锂混合物3、磷酸三甲酚酯2、二硫化...