The present invention relates to a woven bag material formula of antistatic and flame retardant plastics, which is characterized in that the composition of raw materials by weight portion of the polypropylene: 95; linear low density polyethylene: 5 8; antioxidant 1010:0.05 0.1; DSTP:0.01 auxiliary antioxidant 0.05; calcium carbonate: 2 4; calcium stearate. 0.1 0.3; titanate coupling agent: 0.2 0.3; antistatic agent: 1 3; 12: 8 decabromodiphenyl oxide; heat and light stabilizer: 0.1 0.3; five two 2 4: antimony oxide, calcium carbonate, the particle size is 324, made of the invention plastic woven bag, with anti electrostatic good flame retardant performance, enhance the safety in the use of plastic bags.
【技术实现步骤摘要】
一种防静电阻燃塑料编织袋原料配方
本专利技术涉及塑料编织袋生产
，尤其涉及一种防静电阻燃塑料编织袋原料配方。
技术介绍
塑料编织袋是一种应用十分广泛的包装带，常见产品有饲料编织袋、腻子粉编织袋、尿素编织袋、蔬菜网眼袋、水果网眼袋、大米编织袋、面粉编织袋、玉米编织袋等，其主要生产工艺是利用塑料原料经塑制造粒、扁丝拉伸、圆织布基、涂膜、印刷、切割、缝纫得到产品，最后打包出厂。塑料编织袋属于易燃物，在生产生活中，塑料编织袋往往会集中使用和存放，一旦有塑料编织袋失火，火势会迅速蔓延，给人们的生命财产安全造成重大危害，因此，在很多应用场合，塑料编织袋需要考虑防火阻燃性能，根据统计，在塑料编织袋引发的火灾中，很大一部分是由于静电产生火花导致火灾发生，因此，考虑防火阻燃效果时，防静电也是其中很重要的一部分。
技术实现思路
本专利技术旨在解决现有技术的不足，而提供一种防静电阻燃塑料编织袋原料配方。本专利技术为实现上述目的，采用以下技术方案：一种防静电阻燃塑料编织袋原料配方，其特征在于，由下列重量份的原料构成：聚丙烯：95份；线性低密度聚乙烯：5-8份；抗氧剂1010：0.05-0.1份；辅助抗氧剂DSTP：0.01-0.05份；碳酸钙：2-4份；硬脂酸钙：0.1-0.3份；钛酸酯类偶联剂：0.2-0.3份；抗静电剂：1-3份；十溴二苯醚：8-12份；热、光稳定剂：0.1-0.3份；五氧化二锑：2-4份。所述的碳酸钙粒度为324。本专利技术的有益效果是：用本专利技术制成的塑料编织袋，具有良好的防静电阻燃性能，增强了塑料编织袋在使用中的安全性。具体实施方式下面结合实施例对本...
【技术保护点】
一种防静电阻燃塑料编织袋原料配方，其特征在于，由下列重量份的原料制作而成：聚丙烯：95份；线性低密度聚乙烯：5‑8份；抗氧剂1010：0.05‑0.1份；辅助抗氧剂DSTP：0.01‑0.05份；碳酸钙：2‑4份；硬脂酸钙：0.1‑0.3份；钛酸酯类偶联剂：0.2‑0.3份；抗静电剂：1‑3份；十溴二苯醚：8‑12份；热、光稳定剂：0.1‑0.3份；五氧化二锑：2‑4份。
【技术特征摘要】
1.一种防静电阻燃塑料编织袋原料配方，其特征在于，由下列重量份的原料制作而成：聚丙烯：95份；线性低密度聚乙烯：5-8份；抗氧剂1010：0.05-0.1份；辅助抗氧剂DSTP：0.01-0.05份；碳酸钙：2-4份；硬脂酸钙：0.1...
【专利技术属性】
技术研发人员：陈宗敏，王金刚，
申请(专利权)人：天津华今集团有限公司，
类型：发明
国别省市：天津,12