The invention discloses a high durable phenolic resin containing copper conductive ink, which is characterized by the following formula according to the weight proportion: 20 copper 50; 15 phenol 20; Formaldehyde Solution 10 30 45 60; sodium hydroxide; zinc 5 15; 2 5 auxiliaries a. The present invention in the traditional use of copper as conductive agent based conductive coatings, while adding zinc powder in the coating, spraying, the zinc copper electrode formed in the coating surface, resulting in the loss of pre consumption of copper zinc powder as conductive materials, thereby protecting copper does not cause oxidation or loss for environmental reasons improve the overall durability, conductive rate.
【技术实现步骤摘要】
一种高耐久含铜酚醛树脂导电油墨
本专利技术涉及油墨领域，特别涉及一种高耐久含铜酚醛树脂导电油墨。
技术介绍
导电材料包含导电塑料和导电橡胶。是将树脂和导电物质混合，用塑料的加工方式进行加工的功能型高分子材料。主要应用于电子、集成电路包装、电磁波屏蔽等领域。导电涂料是在导电材料基础上细化的一种材料，其通过在涂料中添加导电材料并通过聚合方式进行分子包裹，从而获得导电功能。但是，由于涂料是易损物，特别是在恶劣的环境下，涂料的导电性将因环境或因粘附在导电粉体上的导电物氧化，从而使得导电涂料在使用时的导电性能慢慢降低，影响使用效果。
技术实现思路
本专利技术要解决的技术问题是：针对上述现有技术的不足，提供一种高耐久含铜酚醛树脂导电油墨。本专利技术解决其技术问题的解决方案是：一种高耐久含铜酚醛树脂导电油墨，其特征在于，由以下配方按照下列重量份配制而成：铜粉20-50份苯酚15-20份甲醛溶液10-30份氢氧化钠45-60份锌粉5-15份助剂2-5份。一种制备上述高耐久含铜酚醛树脂导电油墨的方法，其特征在于，其制备过程包括以下步骤：（1）将铜粉及锌粉经过微米筛网通过加工成微米级，其粒径分布在60-100μm之间，经处理后加入至苯酚中；（2）将步骤（1）中所述的溶液与甲醛溶液、氢氧化钠共同发生聚合反应，在50-150℃加热固化后，得到中间产物；（3）将步骤（2）所述的中间产物加入助剂，搅拌均匀后，得到高耐久含铜酚醛树脂导电油墨。本专利技术的有益效果是：本专利技术在传统使用铜作为导电涂料的导电剂基础上，同时加入了锌粉，而在涂料喷涂后，由于将在涂料表面形成锌-铜电极，由此在损耗时...
【技术保护点】
一种高耐久含铜酚醛树脂导电油墨，其特征在于，由以下配方按照下列重量份配制而成：铜粉 20‑50份苯酚 15‑20份甲醛溶液 10‑30份氢氧化钠 45‑60份锌粉 5‑15份助剂 2‑5份。
【技术特征摘要】
1.一种高耐久含铜酚醛树脂导电油墨，其特征在于，由以下配方按照下列重量份配制而成：铜粉20-50份苯酚15-20份甲醛溶液10-30份氢氧化钠45-60份锌粉5-15份助剂2-5份。2.一种制备权利要求1所述的高耐久含铜酚醛树脂导电油墨的方法，其特征在于，其制备过程包括以下步骤：（1）将铜...