The invention relates to an automobile parts coating has a damping effect, the coating comprises the following components in part by weight: 70 water 80, Ding Ji 16, 12 rubber acrylate 16 18 copies, 10 copies, 8 polysulfide nitrile 6 8 copies, 24 copies, 20 silicone rubber polyurethane 20 22 copies, 30 copies, 24 PVC resin epoxy resin 32 36 copies, 12 copies, 6 carbon black barium sulfate 10 15 and 28 24 crocidolite fibers. The invention has good damping effect, and can be sprayed on the outer surface of the automobile parts or the automobile, so as to improve the tightness, reduce the vibration, reduce noise, improve the comfort of the automobile and the corrosion resistance between the gaps of the automobile body.
【技术实现步骤摘要】
一种具有阻尼作用的汽车零部件涂料
本专利技术涉及涂料,具体说是一种具有阻尼作用的汽车零部件涂料。
技术介绍
汽车涂料就是指涂装在轿车、吉普车、大客车、大卡车等各种类型的汽车车身及零部件上的涂料,有时也包括一些农机产品如拖拉机、联合收割机和摩托车用涂料,一般系指制造新汽车用的涂料及辅助材料和车辆修补用涂料,汽车作为户外交通工具,有其特殊的使用条件,另外,随着近年来汽车工业的飞速发展,汽车的生产量越来越大,这就使汽车的涂装工艺完全转向高速率和现代化的流水作业;随着我国汽车、特别是旅行车及轿车向高档化发展,对保温、防震、消音涂料的性能提出了更高的要求。鉴于此,本专利技术提供了一种具有阻尼作用的汽车零部件涂料。
技术实现思路
针对上述技术问题,本专利技术提供一种具有阻尼作用的汽车零部件涂料。本专利技术所要解决的技术问题采用以下技术方案来实现:一种具有阻尼作用的汽车零部件涂料,该涂料由以下重量份的组分组成:水70-80份、丁基橡胶12-16份、丙烯酸酯16-18份、聚硫8-10份、丁腈6-8份、硅橡胶20-24份、聚氨酯20-22份、聚氯乙烯树脂24-30份、环氧树脂32-36份、炭黑6-12份、硫酸钡10-15份和青石棉纤维24-28份。作为本专利技术进一步优选方案,该涂料最佳重量份的组分组成为:水75份、丁基橡胶14份、丙烯酸酯17份、聚硫9份、丁腈7份、硅橡胶22份、聚氨酯201份、聚氯乙烯树脂26份、环氧树脂34份、炭黑9份、硫酸钡12.5份和青石棉纤维26份。进一步,所述的水为去离子水。本专利技术的有益效果是:相比现有技术,本专利技术具有良好的阻尼作用,喷涂在 ...
【技术保护点】
一种具有阻尼作用的汽车零部件涂料,其特征在于:该涂料由以下重量份的组分组成:水70‑80份、丁基橡胶12‑16份、丙烯酸酯16‑18份、聚硫8‑10份、丁腈6‑8份、硅橡胶20‑24份、聚氨酯20‑22份、聚氯乙烯树脂24‑30份、环氧树脂32‑36份、炭黑6‑12份、硫酸钡10‑15份和青石棉纤维24‑28份。
【技术特征摘要】
1.一种具有阻尼作用的汽车零部件涂料,其特征在于:该涂料由以下重量份的组分组成:水70-80份、丁基橡胶12-16份、丙烯酸酯16-18份、聚硫8-10份、丁腈6-8份、硅橡胶20-24份、聚氨酯20-22份、聚氯乙烯树脂24-30份、环氧树脂32-36份、炭黑6-12份、硫酸钡10-15份和青石棉纤维24-28份。2.根据权...