The invention relates to a straw degradable environmental protection tableware and a preparation method thereof. The main composition of the tableware is made up of the following components: according to the weight, the percentage is 50 to 69% of the corn stalk, 8 to 20% of the corn flour, 12 to 15% of the electric jade powder, 1 to 1.2% of the zinc powder, and 10 to 20% of the starch. The utility model relates to a straw degradable environmental protection tableware, which is a convenient tableware container molded by plant straw through crushing, stirring, disinfection and the like. The product mainly comprises a bowl, a cup, a tray, a dish, a basin, etc.. The characteristics of local materials, low cost, excellent quality; heat compression; non-toxic harmless, green environmental protection; the production process without waste discharge.
【技术实现步骤摘要】
一种秸秆可降解环保餐具及其制备方法
本专利技术涉及一种用秸秆为主要原料制造秸秆可降解环保餐具及其方法。
技术介绍
“十一五”期间,基于对能源的有效利用以及对环境的保护,我国提出了节能减排的政策,农业节能减排是国家节能减排工作的重要组成部分,特别是农村地区能源的有效利用成为不容忽视的问题。我国大部分农村地区秸秆利用效率地,做好农村能源节约,不仅有利于改变农民传统生活方式,而且能有效改善农村生活条件,推进社会主义新农村建设。目前国内广泛使用的白色泡沫塑料(EPS)为一次性餐具的材料,这种餐具威胁着人类的生存环境,这是一种高分子化合物(聚苯乙烯),暴露在空气中或埋入地下经数十年也不会分解或腐烂,严重破坏和污染土壤和水源,这些白色污染给城市的垃圾场地造成很大的负担,所以其危害程度很大。
技术实现思路
本专利技术的目的是针对上述现有技术中存在的不足之处而提供的一种秸秆可降解环保餐具及其制备方法。本专利技术的目的是通过采取以下措施来实现的:该餐具制取的原料按重量百分比如下:(1)玉米秸秆50~69%;(2)玉米粉8~10%;(3)电玉粉12~15%;(4)锌饮粉1~1.2%;(5)淀粉10~20%;制取方法:(1)玉米秸秆切成10公分段,放入粉碎机中粉碎后,再放入喷粉机内加工成面粉状;(2)将配好的料放入加料桶内,边加入边搅拌,将搅拌均匀后的配料放入模具中加热成型,加热温度在140~160℃,每隔5~6秒起模一次,起模后磨边;(3)将磨边后的餐具转入消毒柜消毒后,用塑料薄膜封口包装。本专利技术使用的淀粉为玉米淀粉,电玉粉为化工用的无毒、无害的食用原料,锌饮粉的作用是增加产 ...
【技术保护点】
一种秸秆可降解环保餐具及其制备方法,其特征在于该餐具的组成按重量百分比为:玉米秸秆50~69%玉米粉8~20%电玉粉12~15%锌钦粉1~1.2%淀粉10~20%。
【技术特征摘要】
1.一种秸秆可降解环保餐具及其制备方法,其特征在于该餐具的组成按重量百分比为:玉米秸秆50~69%玉米粉8~20%电玉粉12~15%锌钦粉1~1.2%淀粉10~20%。2.根据权利要求1所述的一种秸秆可降解环保餐具及其制备方法,其特征在于所用的淀粉为玉米淀粉。3.根据权利要求1所述的一种秸秆可降解环保餐具及其制备方法,其特征在于所用的电玉粉为化工用的无毒、无害的食用原料。4.根据权利要求1所述的一种秸秆可降解...