The invention relates to the technical field of ceramic glaze, especially a porcelain glaze, in accordance with the mass fraction meter comprises the following components: 20-30 parts of three kaolin, two aluminum oxide 15-20, calcite 3-9, Zinc Oxide 3.5-6.8, 2.1-5.4 portions of calcium carbonate, ceramic fiber 5-12, silane coupling agent 3-8, zirconium silicate 4-10 3.6-4.8, talc powder, glass beads 12-18. Using the above formula, the invention of the porcelain glaze products, semi transparent, soft color glaze, glaze less defects, strong liquidity in the firing process, the surface quality and high product quality; in addition, the composition of low cost, easy popularization and application.
【技术实现步骤摘要】
一种骨质瓷釉料
本专利技术涉及瓷釉料
,特别是一种骨质瓷釉料。
技术介绍
建筑卫生陶瓷行业非常注重采用先进的釉料技术,国内已经出现一大批专业性很强的陶瓷釉料和陶瓷熔块、色料公司。建筑卫生陶瓷产品中所用的釉料越来越丰富多样,目前多数陶企使用的釉料产品,类别与用途可以大致分类如下:1、铅釉和无铅釉;2、生料釉与熔块釉;3、一次烧成或二次烧成用釉;4、瓷砖,餐具,卫生陶瓷与电瓷用釉;5、按施釉方法划分的浸釉、喷釉、浇釉;6、高温釉和低温釉;7、高膨胀釉和低膨胀釉;8、烧成气氛氧化焰、中性焰和还原焰;9、颜色釉与无色釉;10、透明釉与乳浊釉;11、光泽釉、无光釉、半无光釉或花纹釉等等。
技术实现思路
本专利技术需要解决的技术问题是提供一种骨质瓷釉料。为解决上述的技术问题,本专利技术的一种骨质瓷釉料,按照质量份数计包括以下组分:高岭土20-30份,三氧化二铝15-20份,方解石3-9份,氧化锌3.5-6.8份,碳酸钙2.1-5.4份,陶瓷纤维5-12份,硅烷偶联剂3-8份,硅酸锆4-10份,滑石粉3.6-4.8份,玻璃微珠12-18份。进一步的,按照质量份数计包括以下组分:高岭土20份,三氧化二铝15份,方解石3份,氧化锌3.5份,碳酸钙2.1份,陶瓷纤维5份,硅烷偶联剂3份,硅酸锆4份,滑石粉3.6份,玻璃微珠12份。进一步的,按照质量份数计包括以下组分:高岭土30份,三氧化二铝20份,方解石9份,氧化锌6.8份,碳酸钙5.4份,陶瓷纤维12份,硅烷偶联剂8份,硅酸锆10份,滑石粉4.8份,玻璃微珠18份。进一步的,按照质量份数计包括以下组分:高岭土23份,三氧 ...
【技术保护点】
一种骨质瓷釉料,其特征在于,按照质量份数计包括以下组分:高岭土20‑30份,三氧化二铝15‑20份,方解石3‑9份,氧化锌3.5‑6.8份,碳酸钙2.1‑5.4份,陶瓷纤维5‑12份,硅烷偶联剂3‑8份,硅酸锆4‑10份,滑石粉3.6‑4.8份,玻璃微珠12‑18份。
【技术特征摘要】
1.一种骨质瓷釉料,其特征在于,按照质量份数计包括以下组分:高岭土20-30份,三氧化二铝15-20份,方解石3-9份,氧化锌3.5-6.8份,碳酸钙2.1-5.4份,陶瓷纤维5-12份,硅烷偶联剂3-8份,硅酸锆4-10份,滑石粉3.6-4.8份,玻璃微珠12-18份。2.按照权利要求1所述的一种骨质瓷釉料,其特征在于,按照质量份数计包括以下组分:高岭土20份,三氧化二铝15份,方解石3份,氧化锌3.5份,碳酸钙2.1份,陶瓷纤维5份,硅烷偶联剂3份,硅酸锆4份,滑石粉3.6份,玻璃微珠12份。3.按照权利要求1所述的一种骨质瓷釉料,其特征在于,按照质量份数计包括以下组分:高岭土30份,三...