一种防蓝光薄膜及制作方法技术

本发明专利技术公开了一种防蓝光薄膜及制作方法，特别是指一种防蓝光强化液；一种防蓝光强化液的配料；一种防蓝光强化液配比；一种防蓝光薄膜的制造方法及产品。本发明专利技术防蓝光薄膜的制作方法，包括以下步骤：可吸收型防蓝光强化液的制备；选取主基材；在主基材的一面均匀涂布上一层已制备好的可吸收型防蓝光强化液；再经热能固化和光能固化制的所述防蓝光薄膜。采用本发明专利技术的制造方法，制造出的防蓝光薄膜其具有以下特征：抗刮性能强、高透射率和微色偏性、针对性有效防护、产品搭配更自由、方便、简单。

Blue light preventing film and manufacturing method thereof

The invention discloses an anti blue thin film and a preparation method thereof, in particular to a strengthening liquid anti blue light; an anti blue strengthening liquid ingredients; a liquid ratio enhanced anti blue; making method and product of anti blue films. The invention provides a preparation method of anti blue film, which comprises the following steps: absorption type anti blue enhanced liquid preparation; selection of the main substrate; on one side of the main base on a uniform coating layer has been prepared absorbable anti blue strengthening fluid; after heat curing and light curing system of the anti blue film. The manufacturing method of the invention, a blue light proof film manufacturing which has the following characteristics: scratch resistance, high transmittance and micro color, for effective protection, product collocation more free, convenient and simple.

【技术实现步骤摘要】
一种防蓝光薄膜及制作方法
本专利技术属于光学材料领域，更具体地，涉及一种防蓝光薄膜及制作方法。
技术介绍
世界卫生组织WHO爱眼协会公布：2006年至2008年因蓝光辐射每年导致全球超过30000人失明。据中华医学会眼科学分会数据显示：在中国4.2亿网民中，63.5％的网民因蓝光、辐射有视力下降、白内障、失明等不同程度的眼疾。现有研究表明，高强度蓝光很容易对眼睛造成伤害，蓝光会加速视网膜黄斑区的细胞氧化，照射甚至会损伤视觉细胞。如果黄斑区长期接触蓝光，会增加年老时期眼睛出现黄斑病变的风险，甚至可能造成视力永久受损。蓝光能穿过角膜及晶体，直达视网膜，严重损害人体九成视力的黄斑区，黄斑区在视网膜的中央，有最多视觉细胞，不只眼睛动过刀的老年人是病变的高危险群，利用散瞳剂来治疗近视的小朋友也要避免蓝光伤害，因为一旦造成出血性黄斑部病变，可能就会永久失明。据统计，目前美国和中国约有超过500万人由于黄斑变化(退化)症而视力衰退或失明，而且每年以40万人的数量增长，在将来的20年中，随着老年人口的增加而加倍增加，针对此病症没有有效的治疗方法，目前只能从预防入手，不让蓝光伤害视力。常见的蓝光来源有自然光、霓虹灯、办公室照明、计算机屏幕光线、手机、水银卤素灯、电视等LED、OLED发光有关的所有3C产品。LED、OLED光源，由蓝光激发LED、OLED黄色荧光粉后产生白光，其光谱曲线不平滑，特别是蓝光波段的峰值(550nm波段)明显高于自然光或白炽灯，得到的白光光谱中蓝光比重较多，过强的蓝光对人眼具有危害。随着社会科技的发展，电子产品和多彩装饰灯光等LED、OLED光已经遍布我们的生活，蓝光的危害变的无处不在。所以为了我们的未来和健康，选择一副功能性的蓝光防护镜片或蓝光防护贴膜保护眼睛已成为我们必不可少的生活用品。目前防蓝光镜片和防蓝光贴膜的制作方式有两种：第一种工艺是采用电镀的方式，即在制作好的镜片或膜层上电镀一层防蓝光镀膜。另一种是在镜片的原料中直接填加色粉，利用注塑成型，成具有防蓝光功能的镜片。但是第一种工艺镀有防蓝光镀膜的镜片或贴膜在实际使用过程中容易被划伤或磨损，使得防蓝光功能受损，因此此种方式使用寿命较短。第二种工艺是注塑成型的镜片，对性能要求较高的镜片却无法适用。同时两种工艺都是对所有光谱都进行了防护，没有针对性(450nm～470nm波段LED、OLED等荧光粉激发最强部分对人体有伤害的蓝色光谱区域针对性防护)，色偏严重：色相值b*＞30(根据研究表明：色相值b*＜20的防蓝光镜片对人眼的刺激性最小、最舒适。)且透射率低。
技术实现思路
针对现有技术的耐刮性差、透射率低、色偏严重、没有针对性防护等不足，本专利技术提供了一种使用防油污、抗指纹、高透光、防蓝光效果佳、色偏轻微且对蓝光的防护更有针对性(对450nm～470nmLED、OLED等荧光粉激发最强部分，对人体伤害最大的蓝色光谱区域针对性有效防护)和对不同需求的产品搭配更自由、方便、简单的防蓝光薄膜的制作方法及产品。本专利技术是这样实现的：一、本专利技术率先采用了聚脂类低聚物调配的强化液与高分子蓝光吸收剂等交联、聚合，而得高分子聚合物——可吸收型防蓝光强化液。其特征在于经强化液与高分子蓝光吸收剂等的交联、聚合而得的防蓝光强化液具有针对450nm～470nmLED、OLED等荧光粉激发最强部分，对人体伤害最大的蓝色光谱区域有效防护。而一般染料、色素粉末、电镀等都是对蓝光波段进行整体防护吸收，皆无法达到这一特征。以下是几种光谱数据对比，相应的一般配料镜片光谱曲线图如图1所示，电镀镜片光谱数据如图2所示，注塑镜片光谱曲线图如图3所示，本专利技术配料镜片光谱曲线图如图4所示。WL(nm)T％WL(nm)T％WL(nm)T％WL(nm)T％WL(nm)T％78096.10077096.10076096.30075096.50074096.90073097.10072097.40071097.70070097.60069097.60068097.40067097.00066096.40065095.90064095.40063095.10062094.80061094.60060094.40059094.10058093.90057093.00056091.90055091.00054090.40053089.60052088.70051087.50050085.60049082.50048079.00047076.00046073.40045070.20044066.90043062.10042049.30041018.0004000.4003900.0003800.0003700.0003600.0003500.0003400.0003300.0003200.0003100.0003000.0002900.0002800.000一般配料镜片光谱数据WL(nm)T％WL(nm)T％WL(nm)T％WL(nm)T％WL(nm)T％78092.90077093.40076093.80075094.70074095.00073095.10072095.00071094.70070094.70069095.00068095.60067096.00066096.10065096.20064096.20063096.00062095.80061095.90060096.40059096.50058095.60057094.70056094.00055093.40054091.50053088.20052085.40051084.60050082.80049079.10048076.20047073.00046067.20045061.30044054.70043047.10042039.00041023.5004004.2003900.0003800.0003700.0003600.0003500.0003400.0003300.0003200.0003100.0003000.0002900.0002800.000电镀镜片光谱数据WL(nm)T％WL(nm)T％WL(nm)T％WL(nm)T％WL(nm)T％78093.60077094.70076095.40075096.00074095.50073094.90072094.30071094.30070095.10069096.00068096.80067096.80066096.00065095.30064095.10063095.70062096.30061096.40060095.60059094.40058093.40057092.70056091.40055088.50054085.30053082.80052080.30051074.20050065.70049059.50048054.90047048.50046044.40045043.20044040.60043039.60042035.00041013.8004000.2003900.0003800.0003700.0003600.0003500.0003400.0003300.0003200.0003100.0003000.0002900.0002800.0本文档来自技高网...

【技术保护点】
一种可吸收型防蓝光强化液：将40%的提供基本性能的寡聚体主体树脂：压克力化的氨基甲酸酯、压克力化的聚酯中的一个；与20%的调整性能的单体稀释剂：单官能基、双官能基与多官能基三类中的一个或多个的丙烯酸酯；单官能基THFA 四氢呋喃丙烯酸酯双官能基HDDA 1，6‑己二醇二丙烯酸酯多官能基TMPTA 三羟甲基丙烷三丙烯酸酯和8%的起聚合、交联反应作用的起始剂充分反应后，再与10%的高分子防蓝光吸收剂和3%的起降低表面张力作用的氟素表面活性剂均匀混合，最后添加19%的溶剂稀释：EAC乙酸乙酯、BAC乙酸丁酯中的一个或两个均匀混合而制得防450nm~470nm蓝色光谱区域的防蓝光强化液。

【技术特征摘要】
1.一种可吸收型防蓝光强化液：将40%的提供基本性能的寡聚体主体树脂：压克力化的氨基甲酸酯、压克力化的聚酯中的一个；与20%的调整性能的单体稀释剂：单官能基、双官能基与多官能基三类中的一个或多个的丙烯酸酯；单官能基THFA四氢呋喃丙烯酸酯双官能基HDDA1，6-己二醇二丙烯酸酯多官能基TMPTA三羟甲基丙烷三丙烯酸酯和8%的起聚合、交联反应作用的起始剂充分反应后，再与10%的高分子防蓝光吸收剂和3%的起降低表面张力作用的氟素表面活性剂均匀混合，最后添加19%的溶剂稀释：EAC乙酸乙酯、BAC乙酸丁酯中的一个或两个均匀混合而制得防450nm~470nm蓝色光谱区域的防蓝光强化液。2.一种防蓝光薄膜的制作方法，其特征在于，包括以下步骤：步骤（1）、制备可吸收型防蓝光强化液：根据权利要求1所述的配比可得；步骤（2）、选取主基材；针对不同的产品，选择相对应的主基材；步骤（3）、把步骤（1）所得的防蓝光强...

【专利技术属性】
技术研发人员：吴进家，
申请(专利权)人：来奇偏光科技中国股份有限公司，
类型：发明
国别省市：福建,35