一种适用酸性溶液止回阀阀体制造技术

技术编号:15388015 阅读:76 留言:0更新日期:2017-05-19 02:24
本发明专利技术公开了一种适用酸性溶液止回阀阀体,具有如下步骤:制备和铸造具有如下重量百分比的钢水:2.14%≤C≤2.24%,0.45≤Si≤0.65%,0.5%≤Mo≤0.7%,0.015≤P≤0.035%,0.015≤S≤0.035%,0.75%≤Cr≤0.95%,0.25%≤Co≤0.35%,1.6≤Ni≤1.8%,痕量≤Cu≤0.20%,余量为铁和不可避免的杂质;本发明专利技术阀体材质合金成分配比适当,阀体内壁耐酸涂层具有耐酸特性,使用寿命长,安全可靠。

Valve body suitable for acid solution check valve

The invention discloses an acidic solution for check valve body, has the following steps: preparation and casting of molten steel with the following weight percent: 2.14% = C = 2.24%, 0.45 = Si = 0.65%, 0.5% = Mo = 0.7%, 0.015 = P = 0.035%, 0.015 = S = 0.035%, Cr = 0.75% ~ 0.95%, 0.25% = Co = 0.35%, 1.6 = Ni = 1.8% = Cu = 0.20%, trace impurities in balance, iron and unavoidable; the invention body material alloy composition is appropriate, the inner wall of the valve body with acid acid coating properties, long service life, safe and reliable.

【技术实现步骤摘要】
一种适用酸性溶液止回阀阀体
本专利技术涉及止回阀制备领域,具体属于一种适用酸性溶液止回阀阀体。
技术介绍
止回阀是指依靠介质本身流动而自动开、闭阀瓣,用来防止介质倒流的阀门,又称逆止阀、单向阀、逆流阀、和背压阀。止回阀属于一种自动阀门,其主要作用是防止介质倒流、防止泵及驱动电动机反转,以及容器介质的泄放。当止回阀通过酸性溶液时,长时间工作会造成阀体内壁腐蚀严重。
技术实现思路
本专利技术的目的是提供一种适用酸性溶液止回阀阀体,阀体材质合金成分配比适当,阀体内壁耐酸涂层具有耐酸特性,使用寿命长,安全可靠。本专利技术的技术方案如下:一种适用酸性溶液止回阀阀体,具有如下步骤:a)制备和铸造具有如下重量百分比的钢水:2.14%≤C≤2.24%,0.45≤Si≤0.65%,0.5%≤Mo≤0.7%,0.015≤P≤0.035%,0.015≤S≤0.035%,0.75%≤Cr≤0.95%,0.25%≤Co≤0.35%,1.6≤Ni≤1.8%,痕量≤Cu≤0.20%,余量为铁和不可避免的杂质;b)钢水浇注成型后,阀体加热至550-600℃并保温1-1.2h,油冷至80-100℃后重新加热至620℃-660℃的温度范围并保温0.6-0.9h,保温期间对阀体内腔进行可控气氛热处理是向热处理炉中通入混合气体,氮气通入量在90~120ml/min,丙烷通入量在14~16ml/min;c)最后对阀体内腔喷涂耐酸涂漆,耐酸涂漆由以下重量份原料组成:水合碱式碳酸镁4-5份,磷酸三苯酯24-26份、水溶性氟化物树脂8-9份、硬脂酸钙3.5-4.5份、磷灰石1.5-2份、气相二氧化硅5-7份、消泡剂2.2-3.2份、颜料0.4-0.6份。所述的耐酸涂漆由以下重量份原料组成:水合碱式碳酸镁4.5份,磷酸三苯酯25份、水溶性氟化物树脂8.5份、硬脂酸钙4份、磷灰石1.8份、气相二氧化硅6份、消泡剂2.7份、颜料0.5份。本专利技术阀体材质合金成分配比适当,阀体内壁耐酸涂层具有耐酸特性,使用寿命长,安全可靠。具体实施方式一种适用酸性溶液止回阀阀体,具有如下步骤:a)制备和铸造具有如下重量百分比的钢水:2.14%≤C≤2.24%,0.45≤Si≤0.65%,0.5%≤Mo≤0.7%,0.015≤P≤0.035%,0.015≤S≤0.035%,0.75%≤Cr≤0.95%,0.25%≤Co≤0.35%,1.6≤Ni≤1.8%,痕量≤Cu≤0.20%,余量为铁和不可避免的杂质;b)钢水浇注成型后,阀体加热至550-600℃并保温1-1.2h,油冷至80-100℃后重新加热至620℃-660℃的温度范围并保温0.6-0.9h,保温期间对阀体内腔进行可控气氛热处理是向热处理炉中通入混合气体,氮气通入量在90~120ml/min,丙烷通入量在14~16ml/min;c)最后对阀体内腔喷涂耐酸涂漆,耐酸涂漆由以下重量份原料组成:水合碱式碳酸镁4.5份,磷酸三苯酯25份、水溶性氟化物树脂8.5份、硬脂酸钙4份、磷灰石1.8份、气相二氧化硅6份、消泡剂2.7份、颜料0.5份。依照本专利技术实施例制得的止回阀阀体检测的各项性能如下:抗拉强度Rm≥560Mpa,屈服强度Re≥340Mpa,冲击吸收功Akv≥23J。在高浓度酸性溶液中浸泡30-40天,内壁无腐蚀现象。本文档来自技高网...

【技术保护点】
一种适用酸性溶液止回阀阀体,其特征在于,具有如下步骤:a)制备和铸造具有如下重量百分比的钢水:2.14%≤C≤2.24%,0.45≤Si≤0.65%,0.5%≤Mo≤0.7%,0.015≤P≤0.035%,0.015≤S≤0.035%,0.75%≤Cr≤0.95%,0.25%≤Co≤0.35%,1.6≤Ni≤1.8%,痕量≤Cu≤0.20%,余量为铁和不可避免的杂质;b)钢水浇注成型后,阀体加热至550‑600℃并保温1-1.2h,油冷至80‑100℃后重新加热至620℃-660℃的温度范围并保温0.6‑0.9h,保温期间对阀体内腔进行可控气氛热处理是向热处理炉中通入混合气体,氮气通入量在90~120ml/min,丙烷通入量在14~16ml/min;c)最后对阀体内腔喷涂耐酸涂漆,耐酸涂漆由以下重量份原料组成:水合碱式碳酸镁4‑5份,磷酸三苯酯24‑26份、水溶性氟化物树脂8‑9份、硬脂酸钙3.5‑4.5份、磷灰石1.5‑2份、气相二氧化硅5‑7份、消泡剂2.2‑3.2份、颜料0.4‑0.6份。

【技术特征摘要】
1.一种适用酸性溶液止回阀阀体,其特征在于,具有如下步骤:a)制备和铸造具有如下重量百分比的钢水:2.14%≤C≤2.24%,0.45≤Si≤0.65%,0.5%≤Mo≤0.7%,0.015≤P≤0.035%,0.015≤S≤0.035%,0.75%≤Cr≤0.95%,0.25%≤Co≤0.35%,1.6≤Ni≤1.8%,痕量≤Cu≤0.20%,余量为铁和不可避免的杂质;b)钢水浇注成型后,阀体加热至550-600℃并保温1-1.2h,油冷至80-100℃后重新加热至620℃-660℃的温度范围并保温0.6-0.9h,保温期间对阀体内腔进行可控气氛热处理是向热处理炉中通...

【专利技术属性】
技术研发人员:吴寿涛
申请(专利权)人:铜陵市经纬流体科技有限公司
类型:发明
国别省市:安徽,34

网友询问留言 已有0条评论