本发明专利技术涉及一种防水透气涂料,由以下重量比材料组成:环氧树脂20份,丙烯酸树脂45份,聚氟乙烯8份,乙酸乙酯10份,新戊二醇2份,成膜剂8份,消泡剂7份,纳米二氧化钛粉6份,硅酸铝9份,丙烯酸纳3份,交联剂4份。本发明专利技术提供的防水透气涂料,采用多种树脂混合,混合物分子聚合,从而预留足够分子空间通过气体,添加金属盐增加涂层的韧性,让涂层可随着无纺布一起弯折,而不至破坏涂层。

Waterproof breathable paint

The invention relates to a waterproof breathable coating, by the weight ratio of epoxy resin material composition: 20 copies, 45 copies of acrylic resin, polyvinyl fluoride acetate 8 copies, 10 copies, 2 copies of neopentyl glycol, film-forming agent 8, defoaming agent 7, nano titanium dioxide powder 6, 9 aluminum silicate a acrylic acid sodium 3, crosslinking agent 4. Waterproof breathable coating provided by the invention, using a variety of hybrid resin, a mixture of molecular aggregation, which set aside enough space through the gas molecules, adding metal salt increases the toughness of the coatings, so that coating can be bent together with non-woven fabrics, and not to damage the coating.

【技术实现步骤摘要】
一种防水透气涂料
本专利技术涉及一种涂料,尤其涉及一种防水透气涂料。
技术介绍
家用割草机的收集袋一般采用无纺布制成,而无纺布具有良好的透气性,所以一般收集袋直接装在割草机的出气口处,这样被气流带来的草叶等就可以直接被收集袋收集。但是,无纺布不具有防水性,当露水较重,或者草坪较湿时,无纺布会很快被水打湿,降低出气的效率。
技术实现思路
本专利技术要解决的技术问题是:提出一种应用于割草机收集袋的即透气又防水的涂料。本专利技术为解决上述技术问题提出的技术方案是:一种防水透气涂料,由以下重量比材料组成:环氧树脂20份,丙烯酸树脂45份,聚氟乙烯8份,乙酸乙酯10份,新戊二醇2份,成膜剂8份,消泡剂7份,纳米二氧化钛粉6份,硅酸铝9份,丙烯酸纳3份,交联剂4份。本专利技术提供的防水透气涂料,采用多种树脂混合,混合物分子聚合,从而预留足够分子空间通过气体。添加金属盐增加涂层的韧性,让涂层可随着无纺布一起弯折,而不至破坏涂层。具体实施方式实施例本实施例的防水透气涂料,由以下重量比材料组成:环氧树脂20份,丙烯酸树脂45份,聚氟乙烯8份,乙酸乙酯10份,新戊二醇2份,成膜剂8份,消泡剂7份,纳米二氧化钛粉6份,硅酸铝9份,丙烯酸纳3份,交联剂4份。本专利技术不局限于上述各实施例,凡采用等同替换形成的技术方案,均落在本专利技术要求的保护范围。

【技术保护点】
一种防水透气涂料,其特征在于,由以下重量比材料组成: 环氧树脂20份,丙烯酸树脂45份,聚氟乙烯8份,乙酸乙酯10份,新戊二醇2份,成膜剂8份,消泡剂7份,纳米二氧化钛粉6份,硅酸铝9份,丙烯酸纳3份,交联剂4份。

【技术特征摘要】
1.一种防水透气涂料,其特征在于,由以下重量比材料组成:环氧树脂20份,丙烯酸树脂45份,聚氟乙烯8份,乙酸...