A high performance meter box shell external use protector, which relates to a distribution equipment production technology field, which is characterized in that: made by weight materials, fluorine resin 23, amino resin 19, six sodium hexametaphosphate 4, vinyl carboxylic ester 4 copies, 3 copies, two sodium hydrogen phosphate chromic anhydride 3.5, phosphate ester of fatty alcohol 3.5, KH 560 silane coupling agent 2, alpha hydroxy isobutyrophenone 2 copies, 13 copies of butyl acetate, antioxidant 5, two amino two phenyl sulfone 5 copies, 34 copies of deionized water. The method of the invention is reasonable, convenient to operate and reasonable in proportion, and can protect the outer wall of the meter box.
【技术实现步骤摘要】
一种高性能电表箱外壳外部使用的保护漆
本专利技术涉及配电设备加工生产
,具体涉及一种高性能电表箱外壳外部使用的保护漆。
技术介绍
电表箱是用于制造低压电缆分支箱箱体的材料是一种树脂基复合材料。箱体的主要组成分为ABS工程塑料、聚碳酸酯透明PC材料、DMC、SMC四种材料注塑、压制而成。箱体的材料由两部分组成:基体—聚酯类树脂;增强材料(简称PC、SMC),所以又称其为透明PC材料、纤维增强的聚酯材料。透明PC材料、纤维增强型不饱和聚酯是一种以不饱和聚酯树脂为基体的复合材料。这种两种材料具有不溶、阻燃可回收特点,后一种材料具有不熔不可回收利用弊端其物理结构为三维网状结构,这四种材料通过功能性填料改性及特种纤维的增强已成为一种高性能的工程材料。而现如今电表箱一般都是裸露在室外、空气当中,这样时间长久容易导致外壳的损伤,容易造成锈蚀、腐蚀等情况,减少了使用寿命。
技术实现思路
本专利技术所要解决的技术问题在于克服现有的技术缺陷提供一种方法合理、操作方便、配比合理、能够保护电表箱外壁一种高性能电表箱外壳外部使用的保护漆。本专利技术所要解决的技术问题采用以下的技术方案来实现:一种高性能电表箱外壳外部使用的保护漆,其特征在于:由以下重量份的材料制成,氟树脂23份、氨基树脂19份、六偏磷酸钠4份、乙烯基羧酸酯4份、磷酸氢二钠3份、铬酸酐3.5份、磷酸脂肪醇酯3.5份、KH-560硅烷偶联剂2份、α-羟基异丁酰苯2份、防老剂13份、乙酸丁酯5份、二氨基二苯基砜5份、去离子水34份;包括以下的制备步骤,Ⅰ将上述的除液体材料外的其余的材料加热到60-63℃,然后按照600- ...
【技术保护点】
一种高性能电表箱外壳外部使用的保护漆,其特征在于:由以下重量份的材料制成,氟树脂23份、氨基树脂19份、六偏磷酸钠4份、乙烯基羧酸酯4份、磷酸氢二钠3份、铬酸酐3.5份、磷酸脂肪醇酯3.5份、KH‑560硅烷偶联剂2份、α‑羟基异丁酰苯2份、防老剂13份、乙酸丁酯5份、二氨基二苯基砜5份、去离子水34份。
【技术特征摘要】
1.一种高性能电表箱外壳外部使用的保护漆,其特征在于:由以下重量份的材料制成,氟树脂23份、氨基树脂19份、六偏磷酸钠4份、乙烯基羧酸酯4份、磷酸氢二钠3份、铬酸酐3.5份、磷酸脂肪醇酯3.5份、KH-560硅烷偶联剂2份、α-羟基异丁酰苯2份、防老剂13份、乙酸丁酯5份、二氨基二苯基砜5份、去离子水34份。2.根据权利要求1所述的一种高性能电表箱外壳外部使用的保护漆,其特征在于:包括以下的制备步骤,Ⅰ将上述的除液体材料外...
【专利技术属性】
技术研发人员:陈炎,陈伟,程付军,
申请(专利权)人:滁州思达机电有限责任公司,
类型:发明
国别省市:安徽,34