The invention discloses a method for reducing lead-acid battery plate floating on the surface of the powder, the plate by the lead plate grid coated with paste form. This method maintains the paste components, mixing process and coating process under the same conditions, the harmonic paste temperature control at 50 to 60 DEG C. The present invention by reducing harmonic paste temperature, reduce the coating plate surface floating powder, this method is very simple and easy to implement, effectively reduce the lead pollution in production site, to provide a good working environment for production workers. The invention is suitable for the lead-acid battery with various specifications.
【技术实现步骤摘要】
降低铅酸蓄电池极板表面浮粉的方法
本专利技术涉及一种铅酸蓄电池极板生产过程中降污方法,具体地讲,本专利技术涉及一种降低铅酸蓄电池极板表面浮粉的方法。
技术介绍
极板是铅酸蓄电池的重要组成部件,极板的基础件是铅质板栅,板栅经涂铅膏工艺之后形成极板。由于板栅和铅膏都是铅制品,在涂铅膏期间极板表面易积聚浮粉。此环境下的浮粉富含铅,随风而动的浮粉已成为生产现场的污染源之一。当今,国家对铅酸蓄电池制造业的监督很严,各地的制造商也十分重视生产现场的环保管控,按规定配置了相应的空气净化装置。但是,该技术措施仅是解决现象问题,而没有从根本上消除污染源。所以,生产现场难免不发生超量铅污染。由于铅质浮粉对人体有极大的危害,必须尽量从源头上消除铅质浮粉,确保在岗职工的身体健康。
技术实现思路
本专利技术主要针对现有技术在生产现场中产生超量浮粉的问题,提出一种降低铅酸蓄电池极板表面浮粉的方法,该方法简便,实施容易、降浮粉效果明显,最重要是不降低配套产品的电性能。本专利技术通过下述技术方案实现技术目标。降低铅酸蓄电池极板表面浮粉的方法,所述极板由铅质板栅外涂铅膏而形成。其改进之处在于:该方法在保持铅膏组分配置、搅拌工艺和涂布工艺不变的条件下,将调和铅膏温度控制在50~60℃范围内。本专利技术与现有技术相比,具有以下积极效果:1、降低调和铅膏温度,方法简单、易实现。2、低温调和的铅膏粘度适中,涂布质量好,产生浮粉量少。3、在板栅上涂布低温调和铅膏形成极板,用该种极板制成的铅酸蓄电池电性能不变。具体实施方式下面通过实施例与对比例的性能测试来进一步说明本专利技术。本专利技术是一种降低铅酸蓄电 ...
【技术保护点】
一种降低铅酸蓄电池极板表面浮粉的方法,所述极板由铅质板栅外涂铅膏而形成;其特征在于:该方法在保持铅膏组分配置、搅拌工艺和涂布工艺不变的条件下,将调和铅膏温度控制在50~60℃范围内。
【技术特征摘要】
1.一种降低铅酸蓄电池极板表面浮粉的方法,所述极板由铅质板栅外涂铅膏而形成;其特征在于:该方...
【专利技术属性】
技术研发人员:陆网珍,夏文强,周海波,
申请(专利权)人:双登集团股份有限公司,
类型:发明
国别省市:江苏,32