The invention relates to a process for producing wear-resistant aluminum alloy materials, belonging to the technical field of alloy materials. Includes the following components by weight is prepared by aluminum 20-30, iron 5-15, carbon 0.25-0.5, 0.7-1.6, 13-23 silicon, tungsten chromium, titanium 1.1-2.1 0.3-1.5, Mn 3-6 parts, 0.12-2.1 parts, 0.01-0.03 parts of boron phosphorus and metal oxide 5-10; the components are mixed evenly after the vacuum smelting cast ingot preheating, heating, hot pressing, annealing and fine processing, the material was obtained after annealing. The invention has the advantages of good abrasion resistance, long service life and low production cost, and the invention has high technical content, safe and reliable use, wide application field and remarkable economic effect.
【技术实现步骤摘要】
一种耐磨铝合金材料的生产工艺
本专利技术涉及一种合金材料的生产工艺,尤其是一种耐磨铝合金材料的生产工艺,属于合金材料
技术介绍
合金材料是一种混合物。在很多领域都发挥了很大的作用,代替了很多传统的材料。合金材料按其组成分为金属与金属合金材料、非金属与金属合金材料、非金属与非金属合金材料。与普通单增强相合金材料比,其冲击强度、疲劳强度和断裂韧性显著提高,并具有特殊的热膨胀性能。各类型合金都有以下通性:(1)多数合金熔点低于其组分中任一种组成金属的熔点;(2)硬度一般比其组分中任一金属的硬度大;(特例:钠钾合金是液态的,用于原子反应堆里的导热剂)(3)合金的导电性和导热性低于任一组分金属。利用合金的这一特性,可以制造高电阻和高热阻材料。还可制造有特殊性能的材料;(4)有的抗腐蚀能力强(如不锈钢)如在铁中掺入15%铬和9%镍得到一种耐腐蚀的不锈钢,适用于化学工业。但现有的合金材料其耐磨性能较差。
技术实现思路
本专利技术的目的是克服传统合金材料耐磨性能的不足,提供一种耐磨铝合金材料的生产工艺。本专利技术的目的是通过以下技术方案实现的:一种耐磨铝合金材料的生产工艺,其特征是,包括以下各组份按重量份制备而成:铝20-30份、铁5-15份、碳0.25-0.5份、硅0.7-1.6份、铬13-23份、钨1.1-2.1份、钛0.3-1.5份、锰3-6份、硼0.12-2.1份、磷0.01-0.03份、金属氧化物5-10份;将各组份混合均匀后依次经过真空冶炼铸成锭、预热加温、热压成型、退火保温、细加工成型、退火后得到该材料。一种耐磨铝合金材料的生产工艺,其特征是,包括以下 ...
【技术保护点】
一种耐磨铝合金材料的生产工艺,其特征是,包括以下各组份按重量份制备而成:铝20‑30份、铁5‑15份、碳0.25‑0.5份、硅0.7‑1.6份、铬13‑23份、钨1.1‑2.1份、钛0.3‑1.5份、锰3‑6份、硼0.12‑2.1份、磷0.01‑0.03份、金属氧化物5‑10份;将各组份混合均匀后依次经过真空冶炼铸成锭、预热加温、热压成型、退火保温、细加工成型、退火后得到该材料。
【技术特征摘要】
1.一种耐磨铝合金材料的生产工艺,其特征是,包括以下各组份按重量份制备而成:铝20-30份、铁5-15份、碳0.25-0.5份、硅0.7-1.6份、铬13-23份、钨1.1-2.1份、钛0.3-1.5份、锰3-6份、硼0.12-2.1份、磷0.01-0.03份、金属氧化物5-10份;将各组份混合均匀后依次经过真空冶炼铸成锭、预热加温、热压成型、退火保温、细加工成型、退火后得到该材料。2.根据权利要求1所述的一种耐磨铝合金材料的...