The invention discloses a method for preparing printing plate sealing liquid, mixing prepared by sodium fluoride, phosphate and deionized water, the sealing liquid prepared by the invention can reduce the surface tension of the base, reducing the adsorption, the layout of the enhanced hydrophilicity and stability, colorless base requirements after sealing at the same time, and has high corrosion resistance and good abrasion resistance. Moreover, the sealing liquid prepared by the invention can participate in the production operation of the printing plate at normal temperature, increase the yield of the printing plate and save the cost.
【技术实现步骤摘要】
一种印刷版材用封孔液制备方法
本专利技术涉及印刷CTP版材版材加工的
,更具体地讲,是关于一种印刷版材用封孔液制备方法。
技术介绍
阳图热敏CTP版材在使用之前需堵塞阳极氧化膜孔隙,使之丧失部分或全部吸附能力,从而提高阳极氧化膜的防污染、抗蚀性能力,这样的处理过程被称为封孔处理。如不加处理,直接涂布感光液,版面就会牢固地将感光液吸附住,这种版材即使经曝光、显影或用溶剂洗涤,感光液也仍然不能完全脱离而被吸附在版面上,空白部分极易被污染,提墨、印刷时印版就会上脏。封孔处理可以降低版基表面的张力,减小吸附性,增强版面的亲水性和稳定性,同时要求封孔后的版基无色,并具有良好的抗蚀性和高耐磨性。封孔机理比较复杂,这是因为在不同介质中进行封孔处理,其反应速度,封孔后的铝版表面色泽,进入微孔中的介质含量、亲水性等都有所不同,简单来说,就是使膜层表面的三氧化二铝产生结晶水,增大体积,以堵塞部分微孔。经封孔处理后,阳极氧化膜的体积大约增大33%。
技术实现思路
专利技术目的:针对现有技术的不足,申请人经过多次实践改进,设计了一种印刷版材用封孔液制备方法,本专利技术制备的封孔液能够有效降低版基表面的张力,减小吸附性,增强版面的亲水性和稳定性。技术方案:为了实现上述专利技术目的,本专利技术所采用的技术方案为:一种印刷版材用封孔液制备方法,由氟化钠、磷酸及去离子水进行搅拌混合制得,按重量计,由以下组分组成:氟化钠4.5%磷酸0.8‰余量为去离子水。本专利技术优选的实现方式为:本品仍由氟化钠、磷酸及去离子水进行搅拌混合制得,按重量计,由以下组分组成:氟化钠4.8%磷酸0.9‰余量为 ...
【技术保护点】
一种印刷版材用封孔液制备方法,由氟化钠、磷酸及去离子水进行搅拌混合制得,按重量计,由以下组分组成:氟化钠 4.5%磷酸 0.8‰余量为去离子水。
【技术特征摘要】
1.一种印刷版材用封孔液制备方法,由氟化钠、磷酸及去离子水进行搅拌混合制得,按重量计,由以下组分组成:氟化钠4.5%磷酸0.8‰余量为去离子水。2.一种印刷版材用封孔液制备方法,由氟化钠、磷酸及去离子水进行搅拌混合制得,按重量计,由以下组分组成:氟化钠4.8%磷酸0.9‰余量为去离子水。...