The invention discloses a novel flame retardant wood modified liquid, which comprises the following raw materials: castor butyl oleate sodium sulfate, sodium montmorillonite, three glycerol esters of fatty acids, accounting for amino sulfonic acid sodium salt, glycerin monostearate, mica, sodium phosphite, flame retardant, water amount. The invention has the advantages that can improve the strength and flame retardant properties of wood, its density, hardness, bending strength and elastic modulus were better performance can enhance the wood and prolong the service life of wood; the preparation process is simple, convenient operation, stable quality, high production efficiency, and improve the resistance high temperature insulation performance, improve, improve the quality of the products, large scale.
【技术实现步骤摘要】
一种新型木材阻燃改性液
本专利技术涉及一种木材改性液,特别涉及一种新型木材阻燃改性液。
技术介绍
随着国家经济建设的发展及人民生活水平的提高,人们对木材的需求量越来越大。而天然林保护工程的实施,使得木材供求矛盾更加突出。为缓解供需矛盾,我国已营造了大面积的工业人工林。人工林木材虽然有速生丰产等优点,但是人工速生林木材的物理力学性能较差,密度低,材质松软,易产生干缩变形。为了拓展人工林木材的应用范围,提高人工林木材的经济价值,人们用各种方法对人工速生林木材进行改性。目前研究较多的是采用热固性树脂对木材进行浸渍处理,热固性合成树脂在固化后耐水性强,不流失,而且强度高,受热不软化,适用于浸渍木材。用于浸渍木材的合成树脂必须具有粘度低的特点,否则无法对木材进行充分浸渍。聚合度的高低是决定树脂浸渍处理效果好坏的主要因素,所以应采用低聚合度的初期树脂。现有浸渍处理方式是将木材浸渍在水溶性低分子量的树脂溶液中,树脂扩散进入木材细胞中并使木材增容,经干燥除去水分,树脂由于加热而固化,生成不溶于水的聚合物,沉积填充于细胞内,或与木材组分发生交联,从而使木材密度增大、硬度及强度提高、尺寸稳定性改善。
技术实现思路
本专利技术的目的在于克服现有技术中所存在的上述不足,提供一种新型木材阻燃改性液。为了实现上述专利技术目的,本专利技术提供了以下技术方案:一种新型木材阻燃改性液,包括如下重量份的原料:蓖麻油酸丁酯硫酸钠0.5-1份、钠基蒙脱土2-4份、三硬脂酸甘油酯占1-3份、氨基磺酸钠0.2-0.5份、硬脂酸单甘油酯1-1.5份、云母1-2份、亚磷酸钠0.1-0.5份、阻燃剂1-1.5 ...
【技术保护点】
一种新型木材阻燃改性液,其特征在于,包括如下重量份的原料:蓖麻油酸丁酯硫酸钠 0.5‑1份、钠基蒙脱土 2‑4份、三硬脂酸甘油酯占 1‑3份、氨基磺酸钠 0.2‑0.5份、硬脂酸单甘油酯 1‑1.5份、云母 1‑2份、亚磷酸钠 0.1‑0.5份、阻燃剂 1‑1.5份、水适量。
【技术特征摘要】
1.一种新型木材阻燃改性液,其特征在于,包括如下重量份的原料:蓖麻油酸丁酯硫酸钠0.5-1份、钠基蒙脱土2-4份、三硬脂酸甘油酯占1...
【专利技术属性】
技术研发人员:曾宇,
申请(专利权)人:什邡市美的一家木业有限责任公司,
类型:发明
国别省市:四川,51