The invention relates to a synthesis of polyvinyl acetal modified phenolic resin, the technical scheme is as follows: weigh polyvinyl acetal phenolic resin 100 150g butanol 6 8g inhibitor, 4-methoxyphenol 0.1g catalyst, butyl titanate 0.01g, added to the three flasks with a thermometer, the temperature to 65 degrees. Dropping 22G diisocyanate IPDI, the temperature control in 70 75 degrees, 2.5h reaction. The content of NCO group was analyzed by infrared spectrometer. When the peak of NCO disappeared completely, the heating reaction was stopped, and the polyvinyl alcohol acetal modified phenolic resin was obtained.
【技术实现步骤摘要】
本专利技术涉及一种聚乙烯醇缩醛改性酚醛树脂的合成,属于合成化学领域。
技术介绍
随着平板显示技术的不断更新换代,触摸屏作为一种新技术被不断的应用于手机、电脑等产品中,特别是在移动互联网大潮的驱使下,越来越多的平板显示产品采用电容式触控技术。电容式触控技术在多触点设计、手势辨识、反应速度、灵敏度、耐用性、光学特性等方面比传统的电阻式触控技术具有优势。按照目前的生产工艺,电容式触摸屏在制造时需要用到一种粘接材料将各层透明材料组装起来,以消除牛顿环和彩虹现象,减少光线的散射损失,提高平板显示器的亮度和对比度。以前粘接材料一般采用OCA(光学透明胶OpticallyClearAdhesive)胶带,但是LOCA(液态光学透明胶)相对成本较低,胶层厚度灵活可控,更适合于不规则面和中大尺寸屏幕的贴合。
技术实现思路
本专利技术所要解决的技术问题是提供一种聚乙烯醇缩醛改性酚醛树脂的合成,该树脂用于光学透明胶。本专利技术解决上述技术技术方案如下:准确称取聚乙烯醇缩醛酚醛树脂100-150g、正丁醇6-8g、阻聚剂对羟基苯甲醚0.1g、催化剂钛酸丁酯0.01g,加入到带有温度计的三口烧瓶中,升温至65度,开始滴加22g二异氰酸酯IPDI,将温度控制在70-75度,反应2.5h。用红外光谱仪分析NCO基团的含量,待NCO的峰完全消失时,停止加热反应,得到聚乙烯醇缩醛改性酚醛树脂。本专利技术的有益效果是:本专利技术合成的树脂具有较高的折射率,而且具有很好的耐黄变性,用来制作更高端的液态光学透明胶,具有很好的应用价值。另外,合成反应工艺简单、容易控制,不需要使用特殊的设备,无溶剂, ...
【技术保护点】
一种聚乙烯醇缩醛改性酚醛树脂的合成,其特征在于,包括:准确称取聚乙烯醇缩醛酚醛树脂100‑150g、正丁醇6‑8g、阻聚剂对羟基苯甲醚0.1g、催化剂钛酸丁酯0.01g,加入到带有温度计的三口烧瓶中,升温至65度,开始滴加22g二异氰酸酯IPDI,将温度控制在70‑75度,反应2.5h,用红外光谱仪分析NCO基团的含量,待NCO的峰完全消失时,停止加热反应,得到聚乙烯醇缩醛改性酚醛树脂。
【技术特征摘要】
1.一种聚乙烯醇缩醛改性酚醛树脂的合成,其特征在于,包括:准确称取聚乙烯醇缩醛酚醛树脂100-150g、正丁醇6-8g、阻聚剂对羟基苯甲醚0.1g、催化剂钛酸丁酯0.01g,加入到带有温度计的三口烧瓶中,升温至65度,开始滴加22g二异氰酸酯IPDI,将温度控制在70-75度,反应2.5h,用红...