一丁基氧化锡是一种重要的化工原料。工艺流程简述：将一丁基氯化锡水溶液经高位槽放入主反应釜，同时将固碱和水加入溶解槽，配制成10%碱溶液，加入碱高位槽，控制反应温度在 25—55℃（夹套通入冷冻水），一次反应结束。将物料转入二次反应釜，继续滴碱，升温至 85—95℃保温反应，结束后降温至50℃以下。将反应物料打入周转釜，并进行离心脱水，将滤饼加入回转干燥器烘干，经粉碎后包装得成品一丁基氧化锡。水相加入固体离子膜烧碱，反复套用，多次套用在水相中产生氯化钠固体，将水相离心，分离出氯化钠的固体。

Process for producing butyl tin oxide

Butyl tin oxide is an important chemical raw material. Process Description: a stannous chloride solution by high tank into the main reactor, while the solid alkali and water into the dissolution tank, prepared 10% alkali solution, adding alkali high trough, controlling the reaction temperature in the 25 - 55 C (jacket into the frozen water), the end of a reaction. The material into the two reactor, continue to drop alkali, heating to 85 to 95 DEG C reaction, after cooling to 50 DEG C. The reaction material is put into the turnover kettle, and the centrifugal dehydration is carried out, and the filter cake is added to the rotary dryer to dry. The aqueous phase is added into the solid ionic membrane caustic soda and is repeatedly applied, and the sodium chloride solid is generated in the aqueous solution for several times.

【技术实现步骤摘要】
工艺流程简述将一丁基氯化锡水溶液经高位槽放入主反应釜，同时将固碱和水加入溶解槽，配制成10%碱溶液，加入碱高位槽，控制反应温度在25—55℃（夹套通入冷冻水），一次反应结束。将物料转入二次反应釜，继续滴碱，升温至85—95℃保温反应，结束后降温至50℃以下。将反应物料打入周转釜，并进行离心脱水，将滤饼加入回转干燥器烘干，经粉碎后包装得成品一丁基氧化锡。水相加入固体离子膜烧碱，反复套用，多次套用在水相中产生氯化钠固体，将水相离心，分离出氯化钠的固体。反应涉及的方程式为（以一丁基氯化锡计反应转化率99.9%，收率为99.8%）：

【技术保护点】
一种一丁基氧化锡生产工艺。

【技术特征摘要】
1.一种一丁基氧化锡生产工艺。2....

【专利技术属性】
技术研发人员：胡江海，张晓磊，于飞，
申请(专利权)人：宁夏际华环境安全科技有限公司，
类型：发明
国别省市：宁夏;64