The present invention relates to an ultra-high pumping performance of super high strength concrete, which comprises: 300-380 portions of cement, sand stone 570-590, 1100-1200, water 160-175, 30~35 powder, 135-150 fly ash, zeolite 15-25, 70-90 powder, 15-20 water reducing agent, silicon powder 22-35 parts, lead gas agent 0.03-0.04; the preparation steps are as follows: (1) according to a predetermined ratio of raw materials; (2) the air entraining agent adding water reducing agent, mixing evenly; (3) the sand and stone into the blender, and then turn into powder, cement, fly ash, zeolite powder, slag and silica fume mixing join the steps; (2) in the mixture, adding water; the invention adopts the proper proportion of materials, prepared with ultra-high pumping performance of super high strength concrete with high strength, low viscosity and good pumping performance.
【技术实现步骤摘要】
本专利技术涉及混凝土
,尤其涉及一种具有超高泵送性能的超高强混凝土及其制备方法。
技术介绍
随着建筑业的发展,城市化进程的推进,超高层建筑的数量越来越多,这些超高层建筑一方面需要所用的混凝土有超高的强度等级,另一方面需要混凝土有良好的工作性能,可以直接泵送到较高的垂直高度。因此有必要专门开发这种超高强度、低粘度和泵送性能好的混凝土。
技术实现思路
本专利技术的目的是提供一种使用采用价格低廉的原材料,采用合适的原料配比,制得具有超高强度、低粘度和泵送性能好的的具有超高泵送性能的超高强混凝土,本专利技术方法生产工艺简单、施工方便。为实现上述目的,本专利技术具有超高泵送性能的超高强混凝土包括以下重量份数的组分:水泥300-380份,砂子570-590份,石子1100-1200份,水160-175份,石粉30~35份,粉煤灰135-150份,沸石粉15-25份,矿粉70-90份,减水剂15-20份,硅粉22-35份,引气剂0.03-0.04份;其中,上述组分的技术指标如下:水泥:强度等级≥42.5Mpa,3d≥22Mpa,28d≥47Mpa;砂:Ⅱ区中砂,含泥量≤2.0%,泥块含量≤0.5%;石子:5-25mm碎石,含泥量≤0.5%,泥块含量≤0.2%,针片状含量≤8%;石粉:石粉是石头的粉末的通称,白色粉末,300-400目,CaCO3含量≥90%,含铁量≤1%,含镁量≤1%。粉煤灰:
【技术保护点】
一种具有超高泵送性能的超高强混凝土,其特征在于:其包括以下重量份数的组分:水泥300‑380份,砂子570‑590份,石子1100‑1200份,水160‑175份,石粉30~35份,粉煤灰135‑150份, 沸石粉15‑25份,矿粉70‑90份,减水剂 15‑20份,硅粉 22‑35份,引气剂0.03‑0.04份;其中,上述组分的技术指标如下:水泥:强度等级≥42.5 Mpa,3d≥22 Mpa,28d≥47 Mpa;砂:Ⅱ区中砂,含泥量≤2.0%,泥块含量≤0.5%;石子:5‑25mm碎石,含泥量≤0.5%,泥块含量≤0.2%,针片状含量≤8%;石粉:石粉是石头的粉末的通称,白色粉末,300‑400目,CaCO3含量≥90%,含铁量≤1%,含镁量≤1%;粉煤灰:F类Ⅰ级粉煤灰,需水量比≤95% ,烧失量≤5%;沸石粉:二氧化硅含量80‑99%,100‑400目,1‑4mm;矿粉,S95级或S105级活性指数7d≥75% ,28d≥ 95%;硅粉:比表面积2000‑2800m3/㎏;减水剂:聚羧酸系高性能减水剂,浓度≥ 15%;引气剂:AE类引气剂。
【技术特征摘要】
1.一种具有超高泵送性能的超高强混凝土,其特征在于:其包括以下重量份数的组分:
水泥300-380份,砂子570-590份,石子1100-1200份,水160-175份,石粉30~35份,粉煤
灰135-150份,沸石粉15-25份,矿粉70-90份,减水剂15-20份,硅粉22-35份,引气剂
0.03-0.04份;
其中,上述组分的技术指标如下:
水泥:强度等级≥42.5Mpa,3d≥22Mpa,28d≥47Mpa;
砂:Ⅱ区中砂,含泥量≤2.0%,泥块含量≤0.5%;
石子:5-25mm碎石,含泥量≤0.5%,泥块含量≤0.2%,针片状含量≤8%;
石粉:石粉是石头的粉末的通称,白色粉末,300-400目,CaCO3含量≥90%,含铁量≤1%,
含镁量≤1%;
粉煤灰:F类Ⅰ级粉煤灰,需水量比≤95%,烧失量≤5%;
沸石粉:二氧化硅含量80-99%,100-400目,1-4mm;
矿粉,S95级或S105级活性指数7d≥75%,28d≥95%;
硅粉:比表面积2000-28...
【专利技术属性】
技术研发人员:李红伟,南春明,
申请(专利权)人:邢台建工商品混凝土有限公司,
类型:发明
国别省市:河北;13