Fireproof insulation building material, which comprises the following raw materials in parts by weight: 20~50 melamine resin; perlite 15~40; modified attapulgite 5~12; aluminum silicate fiber cotton 5~10; plant fiber powder 3~8; light calcium carbonate powder 10~15; plasticizer 2~6; dispersing agent 1~3 0.5~1.5; crosslinking agent; flame retardant masterbatch 0.6~1.2; 2~5; auxiliary packing 2~8. The invention provides a building material with good thermal insulation, flame retardant effect, improve the fire performance of materials, at the same time, in addition to thermal performance, can realize the storage temperature adjustment function, and high strength materials, improve the mechanical properties and anti stamping properties, and meet the requirements of environmental protection, new building materials.
【技术实现步骤摘要】
本专利技术涉及建筑材料
，具体涉及一种防火保温建筑材料。
技术介绍
在建筑工程中使用的材料统称为建筑材料。建筑材料可分为结构材料、装饰材料和某些专用材料。结构材料包括 木材、竹材、石材、水泥、混凝土、金属、砖瓦、陶瓷、玻璃、工程塑料、复合材料等；装饰材料包括各种涂料、油漆、镀层、贴面、各色瓷砖、具有特殊效果的玻璃等；专用材料指用于防水、防潮、防腐、防火、阻燃、隔音、隔热、保温、密封等。保温材料一般是指导热系数小于或等于0.2的材料。保温材料材料发展很快，在工业和建筑中采用良好的保温技术与材料，往往可以起到事半功倍的效果。传统保温材料只具有单一热阻性能，没有储能调温功能。而且，在抗压性能差，阻燃效果低，导致强度和防火效果差，环保性差，不能满足人们对新型建筑材料的要求。因此，针对上述问题，本专利技术提出了一种新的技术方案。
技术实现思路
本专利技术的目的是提供一种配方合理，具有良好的保温和防火效果，同时，可实现储能调温功能的防火保温建筑材料。本专利技术是通过以下技术方案来实现的：一种防火保温建筑材料，包括以下重量份数的原料组成：密胺树脂 20~50份；膨胀珍珠岩 15~40份；改性凹凸棒土 5~12份；硅酸铝纤维棉 5~10份；植物纤维粉末 3~8份；轻质碳酸钙粉 10~15份；增塑剂 2~6份；分散剂 1~3份；交联剂 0.5~1.5份；阻燃剂 0.6~1.2份；色母粒 ...
【技术保护点】
一种防火保温建筑材料，其特征在于：包括以下重量份数的原料组成：密胺树脂 20~50份；膨胀珍珠岩 15~40份；改性凹凸棒土 5~12份；硅酸铝纤维棉 5~10份；植物纤维粉末 3~8份；轻质碳酸钙粉 10~15份；增塑剂 2~6份；分散剂 1~3份；交联剂 0.5~1.5份；阻燃剂 0.6~1.2份；色母粒 2~5份；辅助填料 2~8份。
【技术特征摘要】
1.一种防火保温建筑材料，其特征在于：包括以下重量份数的原料组成：密胺树脂 20~50份；膨胀珍珠岩 15~40份；改性凹凸棒土 5~12份；硅酸铝纤维棉 5~10份；植物纤维粉末 3~8份；轻质碳酸钙粉 10~15份；增塑剂 2~6份；分散剂 1~3份；交联剂 0.5~1.5份；阻燃剂 0...