The invention discloses a three EPDM material, which relates to the technical field of rubber; it contains three EPDM components and adhesives; the three rubber composition and adhesive quality ratio is 10 15:1 1.5; the three rubber composition contains the following quality copies component: three yuan 50, 20 ethylene propylene rubber anti-aging agent 2 8 copies, 10 copies, 5 antioxidant 2 paraffin 8, N 330 Black 10 20 copies, 10 copies, accelerator CZ5 10 polypropylene 30; the adhesive comprises the following parts by weight of a group points: 50, 20 polyurethane adhesive agent 10 15 copies, 20 copies, 10 accelerator 20 polyether 30; the invention improves the strength and adhesiveness, not easy to crack, prolong the service life, cost savings.
【技术实现步骤摘要】
本专利技术涉及橡胶
,具体涉及一种三元乙丙橡胶材料。
技术介绍
三元乙丙橡胶是乙烯、丙烯以及非共轭二烯烃的三元共聚物,1963年开始商业化生产。每年全世界的消费量是80万吨。EPDM最主要的特性就是其优越的耐氧化、抗臭氧和抗侵蚀的能力。由于三元乙丙橡胶属于聚烯(PA66)烃家族,它具有极好的硫化特性。在所有橡胶当中,EPDM具有最低的比重。它能吸收大量的填料和油而影响特性不大。因此可以制作成本低廉的橡胶化合物。现有的三元乙丙橡胶材料在制作时其成本高,而且强度低,容易开裂。
技术实现思路
本专利技术的目的在于针对现有技术的缺陷和不足,提供一种三元乙丙橡胶材料。为了解决
技术介绍
所存在的问题,本专利技术的一种三元乙丙橡胶材料,它包含三元乙丙橡胶组分与胶粘剂;所述的三元乙丙橡胶组分与胶粘剂的质量比为10-15:1-1.5;所述的三元乙丙橡胶组分包含如下质量份的组分:三元乙丙橡胶20-50份、抗老化剂2-8份、抗氧化剂5-10份、石蜡2-8份、N-330炭黑10-20份、促进剂CZ5-10份、聚丙烯10-30份;所述的胶粘剂包含如下质量份的组分:聚氨酯粘接剂20-50份、活性剂10-15份、促进剂10-20份、聚醚20-30份。本专利技术有益效果为:提高了强度与粘接度,不易开裂,延长使用寿命,节省成本。具体实施方式本具体实施方式采用如下技术方案:一种三元乙丙橡胶材料,它包含三元乙丙橡胶组分与胶粘剂;所述的三元乙丙橡胶组分与胶粘剂的质量比为10-15:1-1.5;所述的三元乙丙橡胶组分包含如下质量份的组分:三元乙丙橡胶20-50份、抗老化剂2-8份、抗氧化剂5-1 ...
【技术保护点】
一种三元乙丙橡胶材料,其特征在于:它包含三元乙丙橡胶组分与胶粘剂;所述的三元乙丙橡胶组分与胶粘剂的质量比为10‑15:1‑1.5;所述的三元乙丙橡胶组分包含如下质量份的组分:三元乙丙橡胶20‑50份、抗老化剂2‑8份、抗氧化剂5‑10份、石蜡2‑8份、N‑330炭黑10‑20份、促进剂CZ5‑10份、聚丙烯10‑30份;所述的胶粘剂包含如下质量份的组分:聚氨酯粘接剂20‑50份、活性剂10‑15份、促进剂10‑20份、聚醚20‑30份。
【技术特征摘要】
1.一种三元乙丙橡胶材料,其特征在于:它包含三元乙丙橡胶组分与胶粘剂;所述的三元乙丙橡胶组分与胶粘剂的质量比为10-15:1-1.5;所述的三元乙丙橡胶组分包含如下质量份的组分:三元乙丙橡胶20-50份、抗老化剂2-8份、...