The invention provides a AZ80 magnesium alloy steel forging process, which comprises the following steps: 1) blank temperature at 550 DEG C to 600 DEG C; 2) at 900 DEG C before the slow heating, heat for 115 minutes at 900 DEG C; 3) at 900 DEG C after rapid heating to the top temperature of 1200 DEG C, top temperature of heat for 120 minutes; 4) after step 3) by way of cold air cooling to room temperature. A kind of AZ80 magnesium alloy steel forging process provided by the invention, by controlling the forging furnace to the isothermal temperature and holding time, can be evenly balanced organization, greatly reducing the hardness of powder forging, the surface hardness of forgings can meet the requirements of application.
【技术实现步骤摘要】
本专利技术涉及钢材
,尤其涉及一种AZ80镁合金钢锻造加热工艺。
技术介绍
钢铁工业从形成到现在得到了突飞猛进的发展，这些钢材中相当大的数量经过机械加工以零件的形式服务于各行各业的领域和场合。随着机械加工的切削速度越来越快，对钢材的工艺也提出了更高的要求。
技术实现思路
为解决现有技术和实际情况中存在的上述问题，本专利技术提供了一种AZ80镁合金钢锻造加热工艺，包括如下步骤：1)毛坯装炉温度在550℃－600℃；2)在900℃之前缓慢加热，在900℃时进行115分钟的保温；3)在 900℃后快速加热至顶温1200℃，顶温下进行120分钟的保温；4）步骤3）之后以空冷的方式冷却到室温。有益效果：本专利技术提供的一种AZ80镁合金钢锻造加热工艺，通过控制锻件进入等温炉的温度和保温时间，即可得到均匀的平衡组织，极大的减小锻件的硬度散差，同时使得锻件的表面硬度完全满足使用要求。具体实施方式下面详细介绍本专利技术技术方案。本专利技术提供了一种AZ80镁合金钢锻造加热工艺，包括如下步骤：1)毛坯装炉温度在550℃－600℃；2)在900℃之前缓慢加热，在900℃时进行115分钟的保温；3)在 900℃后快速加热至顶温1200℃，顶温下进行120分钟的保温；4）步骤3）之后以空冷的方式冷却到室温。有益效果：本专利技术提供的一种AZ80镁合金钢锻造加热工艺，通过控制锻件进入等温炉的温度和保温时间，即可得到均匀的平衡组织，极大的减小锻件的硬度散差，同时使得锻件的表面硬度完全满足使用要求。最后应说明的是：以上所述仅为本专利技术的优选实施例而已，并不用于限制本专利技术，尽管...
【技术保护点】
一种AZ80镁合金钢锻造加热工艺，其特征在于，包括如下步骤：1)毛坯装炉温度在550℃－600℃；2)在900℃之前缓慢加热，在900℃时进行115分钟的保温；3)在 900℃后快速加热至顶温1200℃，顶温下进行120分钟的保温；4）步骤3）之后以空冷的方式冷却到室温。
【技术特征摘要】
1.一种AZ80镁合金钢锻造加热工艺，其特征在于，包括如下步骤：1)毛坯装炉温度在550℃－600℃；2)在900℃之前缓慢加热，在900...
【专利技术属性】
技术研发人员：何拥军，
申请(专利权)人：柳州科尔特锻造机械有限公司，
类型：发明
国别省市：广西;45