A method for preparing anti rust paint, the weight percentage of 7% 10% polyvinyl butyral resin, 30% 45% ethanol, 8% 16% 10% 20% phenolic resin, toluene, 1.5% 3%, 4% 8% rust conversion agent of talcum powder, 5% 9% iron oxide red, 4% 7% 3% Zinc Oxide 6% stabilizer, stirring and placed in the grinder for grinding grinding into powder, and then mixing the powder and 1% 5% water mixing 30min until the formation of thick liquid. The invention of antirust paint and metal surface complexation, rust and long service life, fast drying, convenient use, low cost, high temperature resistant, can be directly sprayed or painted on the metal surface are embroidered, and can also work in 20 DEG C under low temperature.
【技术实现步骤摘要】
本专利技术涉及油漆领域，特别涉及一种防锈漆的配制方法。
技术介绍
金属生锈是最普通、损失最大的一种腐蚀。防锈工作历来是国内外的重大科研课题之一，人们研究出多种措施防止和抑制金属的锈蚀，以涂料防锈便是一种有效的方法。防锈漆可保护金属表面免受大气、海水等的化学或电化学腐蚀的涂料，。目前市面上使用的防锈漆大致为油性和水性两种，油性防锈漆使用方便，价格低廉，但因含有亚硝酸盐、铬酸盐等有毒物质，对操作人员危害较大，国家已限制使用，因此目前水性防锈漆品种日益繁多，水性漆可以分为水溶型、水分散型、水稀释型这三种，水性漆对施工过程中及材质的表面清洁度要求比较高，如果清理得不是很干净，那么水性漆涂出的效果也会受到大大影响。
技术实现思路
为解决上述问题，本专利技术提供了一种防锈漆的配制方法，具体如下：本专利技术的一种防锈漆的配制方法，其特征在于所述的方法为：将重量百分比为7%-10%的聚乙烯醇缩丁醛树脂、30%-45%的乙醇、8%-16%的酚醛树脂、10%-20%的甲苯、1.5%-3%的转锈剂、4%-8%的滑石粉、5%-9%的氧化铁红、4%-7%的稳定剂、3%-6%的氧化锌充分搅拌并放入粉碎机进行粉碎研磨成粉末，粉末大小为50目，然后将粉末和1%-5%的水混合搅拌30min以上直至形成浓稠状液体。优选地，前述稳定剂采用锌铬黄，它能和金属表面及树脂形成高分子络合物，达到形成碱式络合物的能力，这种络合物可和漆料的极性基因进一步络合，生成稳定的交联的络合物以增强漆膜的耐水性和附着力，同时又和铁离子形成络合物，阻止绣的形成和发展。优选地，所述转绣剂由重量百分比32%的柠檬酸和68%的...
【技术保护点】
一种防锈漆的配制方法，其特征在于所述的方法为：将重量百分比为7%‑10%的聚乙烯醇缩丁醛树脂、30%‑45%的乙醇、8%‑16%的酚醛树脂、10%‑20%的甲苯、1.5%‑3%的转锈剂、4%‑8%的滑石粉、5%‑9%的氧化铁红、4%‑7%的稳定剂、3%‑6%的氧化锌充分搅拌并放入粉碎机进行粉碎研磨成粉末，然后将粉末和1%‑5%的水混合搅拌30min以上直至形成浓稠状液体。
【技术特征摘要】
1.一种防锈漆的配制方法，其特征在于所述的方法为：将重量百分比为7%-10%的聚乙烯醇缩丁醛树脂、30%-45%的乙醇、8%-16%的酚醛树脂、10%-20%的甲苯、1.5%-3%的转锈剂、4%-8%的滑石粉、5%-9%的氧化铁红、4%-7%的稳定剂、3%-6%的氧化锌充分搅拌并放入粉碎机进行粉碎研磨成粉末，然后将粉末...